China GIC Cement (3 Bottle Powder + 3 Bottle Liquid)

Contains high-quality fluoro alumina silicate glass, enhancing the cement’s strength and fluoride release properties.
Utilizes polyacrylic acid, which improves the cement’s bonding to tooth structures and enhances its overall performance.
Provides adequate mixing and working time, allowing ample time for application and adjustment before setting begins.
Delivers a compressive strength of ≥50 MPa, providing durable and robust restorations suitable for various dental procedures.
Releases fluoride over time, contributing to the remineralization of the tooth structure and enhancing long-term dental health.
Demonstrates superior wetting properties, which improve the adhesion of the cement to the tooth structure and ensure effective bonding.
Provides radiopacity, allowing for clear visibility on X-rays, which helps in monitoring and assessing the restoration.
Exhibits low solubility, reducing the risk of material loss or degradation over time and ensuring longevity of the restoration.

China Gic (3 Bottle Powder + 3 Bottle Liquid) is an advanced dental restorative material, ideal for a range of dental procedures. This comprehensive kit includes three bottles of powder and three bottles of liquid, ensuring a complete solution for dental restorations.
Renowned for its excellent adhesion and fluoride release, China GIC supports tooth remineralization and promotes long-term dental health. The material is easy to mix, sets rapidly, and offers superior biocompatibility, making it suitable for restoring primary teeth, as well as base lining and filling class III, V, and limited class I cavities.
As a cost-effective option, China GIC delivers high-quality performance without compromising on reliability, making it a trusted choice for dental practitioners.

Category: Dental Cements
Type: Glass-Ionomer Cement
Powder : Fluoro alumina silicate glass
Liquid : Polyacrylic acid
Mixing Time : 60 sec
Working Time : 90sec
Setting Time: 1.5~6 min
Compressive Strength: ≥50 Mpa
Acid-erosion: ≤0.17 mm
Shelf Life : 2 years from the date of manufacturing

3 x 20g powder China Gic
3 x 15ml liquid China Gic
1 x Manual

Shake the powder bottle well every time before use.
Dispense one scoop of powder and two drops of liquid onto the mixing pad (The standard powder-to-liquid ratio is 0.19:0.07)
With a plastic spatula, divide the powder into 2 equal parts.
Mix the first portion with all of the liquid for 15 seconds, then mix the remaining portion with the paste formed for 20 seconds.
The total mixing time should be 60 seconds. Transfer cement to the prepared tooth surface using the suitable instrument and finish the restoration.
Allow 1:30 min to 6:00 min for proper setting.