Prevest Denpro Magma NT Kit – Composite Material

Easy handling due to high viscosity
High polishibility
High strength
Abrasive resistance compared to natural tooth
Excellent polishablity
Natural surface luster
Chameleon effect
Natural fluorescence

Prevest-Denpro Magma NT Composite Kit is low shrinkage composite with fillers in combination of nano silica and zirconia filler. Magma NT is a contemporary silica-zirconia nanoparticle based universal hybrid composite with 80% filler loading. The particle size of the fillers facilitate high polishability and superior surface luster. Natural fluorescence and a superior chameleon effect creates long lasting life like restorations. In combination with Fusion self etch bonding agent and Fusion flowable composites, Magma NT delivers reliable functional-esthetic restorations.
Magma NT is visible light curing composite designed for use in anterior and posterior restorations.
Fusion Bond 7 combines the ingredients needed for etching, priming, and bonding into a ingle adhesive, thereby eliminating separate etching and priming steps of the bonding process.
Fusion Bond 7 adhesive can be used for the bonding of both direct and indirect restorations.
Nano Coat Light Cured Protective Varnish is a protective coating for glass ionomer, composite and temporary restorations.
The Liquid glaze ensures improved aesthetics and increased strength, toughness and protection.
Fusion Flo is an excellent flowable composite that delivers high strength & wear resistance.
It is Characterized by optimum surface affinity, penetrates into most difficult area. Platina Hi-Gloss Composite Polishing Paste is water-soluble, aluminium oxide paste designed for final polishing of anterior and posterior composite restorations and veneers.
Platina Hi-Gloss Polishing Paste results in a final, high luster polished surface.
Indications :
Direct anterior and posterior restorations
Core build ups
Splinting
Indirect Restorations
Class I,II, III, IV, V restorations
Repair of fractured composite/ceramic laminates.

Shades present – A2 – 2, A3 – 2, A3.5 – 1, B2 – 1, B3 – 1
Composition :
BISGMA,
Bisphenol A diethoxy methacrylate
UDMA,
TEGDMA
Silanated barium glass powder 0.2-2 microns
Nano zirconium oxide powder
Amorphous silica powder
Total inorganic filler content 80%
1) Curing Time : 40 sec.
2) Depth of cure : 1.0 (Opaque shade) 1.5 (Other shade)
3) Compressive Strength : 300 MPa
4) Flexural Strength : 140 – 150 MPa
Storage Conditions : Store at temperature between 10°C to 24°C. Close the cap carefully after use. Keep away from moisture. Shelf life not affected after opening if stored in a cool dry place.
Shelf Life : 3years from the date of manufacturing.

7 X 4g Syringes ( A2 x 2 , A3 x 2, A3.5 x 1 , B2 x 1, B3 x 1)
1 X 5ml bottle Fusion Bond 7
1 X 5ml bottle Fusion Nano Coat
1 x 2g Syringe Fusion Flo-A2 shade
1 x 4g Syringe Platina Hi Gloss
20 x Micro Brushes
10 x Applicator tips
1 x Instruction Manual

Clean the tooth to be treated and adjacent teeth with a brush and prophy paste.
Select the shade using VITA Shade Guide.
Prepare the cavity using conservative cavity technique No residual amalgam or other base material should be left in the cavity.
Cover the area close to the pulp with hard setting CAL-LC Light Cure Calcium Hydroxide paste.
Apply Fusion Bond 7 dentine bonding agent with a disposable brush to the entire cavity. Ensure thorough wetting of the entire cavity. Allow 20 sec air drying and re apply another coat of dentine bonding agent. Remove excess solvent by gently drying with dry air for at least 5sec to ensure uniform glossy surface.
Cure adhesive for 20-30 sec using standard curing light.
Remove Magma NT syringe cap and dispense material onto a mixing pad.
Place the material into the cavity using a suitable placement instrument. Contour the material in the cavity.
Light cure for 40 sec using standard curing light.
When necessary build in increments of 2mm maximum using a layering technique.